I agree about the welds, what you made ins't a crucial part so don't worry about it, but your welds seem to be on the colder side and a porous, If you're using flux-core there's not much you can do about porosity, but if it's a gas mig try adding more gas flow and higher heat with slightly lower wire speed so that you can get flatter more consistent beads, also when mig welding for a nice even finish make little cursive L's with the torch while you're running your bead. Chucke2009 would be an excellent YouTube channel to watch to learn how to get better with your machine.
|